202 Stainless Steel Plate

Name: 202 Stainless Steel Plate
SKU: 0

202 stainless steel is one of the 200 series of stainless steel, which is a stainless steel with low nickel content and high manganese content, because it is a stainless steel developed to save nickel, so its nickel content is relatively low.

Phone ：+86 13225418790

WhatsApp : +86 13225418790

Email : admin@jatsteel.com

Contact Us

Product Description

Product Display

202 stainless steel is an austenitic chromium-nickel-manganese alloy. It has high ductility, good corrosion resistance and excellent toughness in both high and low temperature environments. 202 stainless steel is one of the most widely used 200 series stainless steel. 202 stainless steel, the austenitic structure is stabilized by the addition of nickel and manganese, thereby preventing the formation of harmful phases, such as sigma phase or chromium carbide. The high nickel content also improves the corrosion and oxidation resistance of the steel at high temperatures.

Product Parameters

Product Name	202 Stainless Steel Plate
Type	Plate
Thickness	0.3mm-200mm
Length	2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.
Width	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Scope of Application	Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging,Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.
Certificate	ISO, SGS, BV, etc.
Production Technology	Hot Rolling, Cold Rolling
Edge Processing	Edging, Trimming

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.15	≤1.0	7.5~10.0	17.00~19.00	4.00~6.00	≤ 0.03	≤ 0.06

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥ 520	≥ 275	≥40-50	≤207HB；≤ 95 HRB;≤218HV

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(μohm.in)
7.93	203	17.5	16.3	22