201 Stainless Steel Plate

Name: 201 Stainless Steel Plate
SKU: 0

201 stainless steel generally refers to 201 stainless steel and acid resistant steel. 201 stainless steel refers to the steel that is resistant to the corrosion of weak media such as atmosphere, steam and water, while acid resistant steel refers to the steel that is resistant to the corrosion of chemical corrosive media such as acid, alkali and salt.

Phone ：+86 13225418790

WhatsApp : +86 13225418790

Email : admin@jatsteel.com

Contact Us

Product Description

Product Display

201 stainless steel is composed primarily of iron with between 16 and 18% chromium and up to 0.15% carbon. It also contains small amounts of manganese, nickel, silicon, nitrogen, and copper. It has higher formability than the 300 series grades. In addition, it can be hardened by cold working processes but not heat-treated like 304 or 316 grades. 201 is a high manganese and low nickel stainless steel with low nickel content and poor corrosion resistance. It is widely used in various tabletops, countertops, kitchenware, outdoor decoration engineering, urban decoration industry and low-grade household products. It is also used in medical instruments and automotive parts that require flexibility while maintaining strength under pressure.

Product Parameters

Product Name	201 Stainless Steel Plate
Type	Plate
Thickness	0.3mm-200mm
Length	2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.
Width	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Scope of Application	Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.
Certificate	ISO, SGS, BV, etc.
Production Technology	Hot Rolling, Cold Rolling
Edge Processing	Edging, Trimming

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.15	≤ 0.75	5.50~7.50	16.00~18.00	3.50~5.50	≤ 0.03	≤ 0.06

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥ 520	≥ 275	≥55-60	≤183HB；≤ 100 HRB

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(μohm.in)
7.8	197	15.7	16.2	27